It is a CoCrMoW alloy powder for dental laser selective zone melting, dedicated to the fabrication of additively manufactured porcelain teeth. The formed restorations features corrosion resistance, good biocompatibility, excellent mechanical property, wear resistance and heat resistance.
Wear Resistance
High Sphericity
Low Oxygen Content and Impurities
High Liquidity
Good Biocompatibility
Corrosion Resistance
Heat Resistance
Crowns, bridges, restorations, etc
Main Chemical Composition:
Main Elements (wt%) | ||||
Co | Cr | Mo | W | Si |
Bal. | 24.5-28.5 | 4-6 | 4-6 | ＜1.0 |
C | O | |||
＜0.10 | ＜0.10 | |||
Basic Parameters:
Apparent Density | Tap Density | Hall Flow Rate |
＞4.0g/cm3 | ＞4.5g/cm3 | ＜22s/50g |
Particle Size Distribution:
D10 | D50 | D90 |
15-19μm | 28-35μm | 50-58μm |